English translation for "compound particle"
|
- 复合粒子
Related Translations:
- Example Sentences:
| 1. | For a compound particle , the constituents ' rest mass and also their kinetic energy of motion and potential energy of interactions contribute to the particle ' s total mass
对于复合粒子来说，每个组成粒子的静止质量、动能以及交互作用的位能，都会贡献到粒子的总质量。 | | 2. | Experiments have shown that the nano silicon dioxide particles , nano teflon particles and calcium carbonate / rare earth compound particles have good performance on reducing the friction and resisting the wear
实验表明,添加的纳米二氧化硅微粒、纳米聚四氟乙烯微粒和碳酸钙、稀土复合微粒具有很好的减摩抗磨作用。 | | 3. | The average particle size was from 50nm to 2um . a compounding particle was prepared by coating monodispersed and spherical ultrafine silica particles with titania which obtained by the hydrolysis of ti ( so4 ) 2
以超细单分散球形二氧化硅粒子为载体， ti ( so _ 4 ) _ 2为原料，成功制备了在二氧化硅粒子表面包覆二氧化钛的复合粒子。 | | 4. | Test results showed 1 % silicon dioxide , ptfe3 % and calcium carbonate complex prescriptions ( calcium carbonate and rare earth compound particles are both 1 % ) have good effect on reducing the friction and wear , and has prominent role in industrial applications of high value
试验结果表明:二氧化硅1 % 、 ptfe3 %配方和复合碳酸钙(碳酸钙和稀土元素各1 % )配方具有突出的减摩抗磨作用,具有很高的工业应用价值。 | | 5. | The tio2 / sio2 particle was characterized with scanning electron microscope ( sem ) , infrared spectroscopy and xps . it could be saw from the photo of sem that the compounding particle was still spherical , and there were some tio2 on the surface of sio2 particle . ti - o - si was formed between tio2 and sio2 , and this was confirmed by ft - ir analysis
并运用扫描电镜、红外光谱和xps等检测手段对其进行了表征和测试，从复合粒子的扫描电镜照片中可以看出，复合粒子仍为球形，表面包覆一层tio _ 2 ，与载体氧化硅粒子相比，粒径变化不大；其红外光谱表明， tio _ 2与载体sio _ 2粒子表面有ti ? o ? si键生成，这表明tio _ 2与sio _ 2粒子表面有较强的结合力。 | | 6. | It was the first time that the silica nanoparticles was coated with gd2o3 : eu rare - earth oxides , then the core - shell structure compound particles were obtained . the characterizations showed that the thickness of uniform coating is in 10 - 20nm ; the silica core is linked with the gd2o3 : eu shell by chemical bond si - o - gd ; because of the size effects and interface effects of nano - crystal coating , the diffraction and emission peaks become broadened . and at the same time , the transfer temperature of silica from amorphous to crystal is decreased
首次在纳米sio2表面包覆一层gd2o3 : eu稀土复合氧化物,得到了核-壳结构的复合颗粒，表征结果表明，均匀包覆层的厚度为10 - 20nm ； sio2核和gd2o3 : eu壳层物质之间通过化学键si - o - gd键的作用结合在一起；由于包覆层纳米晶的尺寸效应和界面效应使xrd衍射峰和荧光光谱发射峰出现了宽化现象。 |
- Similar Words：
- "compound paraboliccollector" English translation, "compound paracetamol" English translation, "compound paracetamol tablets" English translation, "compound parameter" English translation, "compound parry" English translation, "compound patent medine" English translation, "compound paths" English translation, "compound pearl" English translation, "compound pellet" English translation, "compound penalty" English translation
|
|
|